DIN磨耗實驗介紹

1. 什么是磨耗實驗？     

磨耗性能是橡膠、硫化膠、熱塑性彈性體等制品的一項重要指標，與材料失效和制品的使用安全性密切相關(guān)。  

耐磨性：物理機械作用力下耐磨耗性 

相對磨損體積：橡膠試樣相對磨損體積（mm3），是指在測試之后與相同條件下與參照膠料的比較得到。 

耐磨性指數(shù)：相同條件下參照膠料體積損耗與試樣體積損耗之比，用百分數(shù)表示  

2. 主要的測試方法    

目前比較普遍采用的三種測試方法是：國標XM一1型磨耗實驗機法(GB/T3903.2-1994)、阿克隆磨耗實驗機法（GB/T1689～1998）和DIN磨耗實驗機法(GB/T9867—1988、ISODIN ISO 4649)。*種方法用帶齒的金屬磨輪垂直壓在試樣上，以一定負荷、一定時間、一定速度，對試樣進行磨耗，測量其磨痕長度，來表示材料的耐磨性能；后兩種方法通過測定試樣在一定條件下，經(jīng)機械摩擦所產(chǎn)生的磨耗減量，來表示材料的耐磨性能。下面主要介紹DIN磨耗實驗。 

3. DIN磨耗實驗    

該機由固定砂紙的旋轉(zhuǎn)滾筒和可水平移動的試樣夾持器組成。滾筒直徑為(150.0±0.2)mm，滾筒速度(40.0±1.0)r/min，磨耗距離為(40.0±0.2)mm，橫向前進滾筒總?cè)?shù)為84r，夾具橫向距離4.2mm/r，試樣夾具荷重2．5N，附加荷重砝碼有2.5N和5.0N兩個。試樣的直徑16mm，厚度至少6mm，試樣厚度少于6mm時，可將兩塊粘貼在一起使用。實驗時，在規(guī)定的接觸壓力(10N)下和給定面積上，采用一定規(guī)格砂紙，對試樣進行摩擦。

圖1. 磨耗測試儀示意圖Figure 1 — Schematic illustration of apparatus  圖2. 試樣制備空心鉆頭示意圖Figure 2 — Example of a hollow drill for test piece preparation  

1. Determination of abrasion resistance    

Abrasion resistance is an important index of Rubber, vulcanized orthermoplastic, and closely related with the life span and safety of materials. 

Terms and definitions 

Abrasion resistance    

The resistance to wear by mechanical action upon a surface

Relative volume loss    

The volume loss, in cubic millimetres, of the test rubber after being subjected to abrasion by an abrasive sheet which will cause a reference compound to lose a defined mass under the same specified conditions of test

Abrasion resistance index    

The ratio of the volume loss of a reference compound to the volume loss of the test rubber measured under the same specified conditions of test and expressed as a percentage

2. Main methods of determining abrasion resistance    

The standards include GB/T1689～1998, GB/T3903.2-1994,

GB/T9867—1988,ISODIN ISO 4649. The methods involve determination of the volume loss due to the abrasive action of rubbing a test piece over a specified grade of abrasive sheet. The result can be reported as a relative volume loss or an abrasion resistance index. 

3. Experiment    

The test apparatus (see Figure 1) consists of a laterally movable test piece holder and a rotatable cylinder to which the abrasive sheet (5.2) is fixed. The cylinder shall have a diameter of and a length of about and shall be rotated at a speed of , the direction of rotation being as indicated in Figure 1. The test piece holder shall have a cylindrical opening, the diameter of which can be adjusted from to and a device for adjusting the length of the test piece protruding from the opening to. The holder shall be mounted on a swivel arm that, in turn, is attached to a sledge that can be moved laterally on a spindle. The lateral displacement of the holder shall be per revolution of the drum (see note 1). Suitable attachments may be provided to rotate the test piece during the test run by rotation of the test piece holder (method B), preferably at the rate of 1 revolution per 50 revolutions of the drum.

Abrasion takes place over one of the end surfaces of the cylindrical test piece (see Figure 1). The abrasive sheet is attached to the surface of a rotating cylindrical drum against which the test piece is held and across which it is traversed. The loss in mass of the test piece is determined and the volume loss is calculated from the density of the material used for the test piece. The volume loss of the test piece is compared to that of a reference compound tested under the same conditions. 

Source:

Rubber, vulcanized or thermoplastic — Determination of abrasion resistance using a rotating cylindrical drum device 

英語：Rubber, vulcanized or thermoplastic –Determination of abrasion resistance using a rotating cylindrical drumdevice (ISO 4649:2002)English version of DIN ISO 4649:2006-11

德語：Elastomere oder thermoplastische Elastomere –Bestimmung des Abriebwiderstandes mit einem Ger?t mit rotierender Zylindertrommel(ISO 4649:2002)Englische Fassung DIN ISO 4649:2006-11