| Cr + Mo + Ni = 0.63 |
| C | Si | Mn | Ni | P | S | Cr | Mo |
| 0.32 - 0.39 | max 0.4 | 0.5 - 0.8 | max 0.4 | max 0.03 | max 0.035 | max 0.4 | max 0.1 |
New opportunities for buyers!
Post free buying requirement of steel C35E (1.1181)
Mechanical properties of steel C35E (1.1181)
| Nominal thickness (mm): | to 16 | 16 - 100 | 100 - 250 | 250 - 500 | 500 - 1000 |
| Rm - Tensile strength (MPa) (+N) | 550 | 520 | 500 | 480 | 470 |
| Nominal thickness (mm): | 0.3 - 3 |
| Rm - Tensile strength (MPa) (+A) | 540 |
| Nominal thickness (mm): | 0.3 - 3 |
| Rm - Tensile strength (MPa) (+CR) | 930 |
| Nominal thickness (mm): | 5 - 10 | 10 - 16 | 16 - 40 | 40 - 63 | 63 - 100 |
| Rm - Tensile strength (MPa) (+C) | 650-1000 | 600-950 | 580-880 | 550-840 | 520-800 |
| Nominal thickness (mm): | to 8 | 8 - 20 | 20 - 50 | 50 - 80 |
| Rm - Tensile strength (MPa) (+QT) | 630 | 600 | 550 | 500 |
| Nominal thickness (mm): | to 8 | 8 - 20 | 20 - 50 | 50 - 80 |
| ReH - Minimum yield strength (MPa) (+QT) | 430 | 380 | 320 | 290 |
| Nominal thickness(mm): | to 16 | 16 - 100 | 100 - 250 |
| Re - Upper yield strength or Rp0.2 - 0.2% proof strength (MPa) (+N) | 300 | 270 | 245 |
| Nominal thickness(mm): | 0.3 - 3 |
| Rp0.2 0.2% proof strength (MPa) (+A) | 430 |
| Nominal thickness(mm): | to 100 | 100 - 250 | 250 - 500 | 500 - 1000 |
| Re - Upper yield strength (MPa) (+N) | 270 | 245 | 220 | 210 |
| Nominal thickness(mm): | 5 - 10 | 10 - 16 | 16 - 40 | 40 - 63 | 63 - 100 |
| Rp0.2 0.2% proof strength (MPa) (+C) | 510 | 420 | 320 | 300 | 270 |
| KV - Impact energy (J) (+QT) | +20° 35 |
| KV - Impact energy (J) (+N) | +20° 27 |
| KV - Impact energy (J) transverse, (+QT) | +20° 22 |
| A - Min. elongation at fracture (%) transverse, (+N) | 15 |
| Nominal thickness (mm): | 5 - 10 | 10 - 16 | 16 - 40 | 40 - 63 | 63 - 100 |
| A - Min. elongation at fracture (%) (+C) | 6 | 7 | 8 | 9 | 9 |
| Nominal thickness (mm): | to 8 | 8 - 20 | 20 - 50 | 50 - 80 |
| A - Min. elongation at fracture (%) longitud., (+QT) | 17 | 19 | 20 | 20 |
| A - Min. elongation at fracture (%) longitud., (+N) | 21 |
| A - Min. elongation at fracture (%) longitud., (+A) | 22 |
| Nominal thickness (mm): | to 16 | 16 - 100 | 100 - 250 |
| A - Min. elongation Lo = 5,65 √ So (%) (+N) | 18 | 19 | 19 |
| Brinell hardness (HBW): (+SH) | 154 - 207 |
| Brinell hardness (HBW): (+A) | 183 |
| Vickers hardness ( HV): (+CR) | 275 |
| Vickers hardness ( HV): (+A) | 170 |
Properties of steel C35E (1.1181)
| Weldability: It can be welded quite well without any precautions. Hardenability: Low hardenability; core quenching in water till a diameter of 12-15 mm; as far as bigger diameters are concerned, it hardens only till a certain depth, inversely proportional to diameter, like all nonalloy steels with medium-high carbon content. |
Equivalent grades of steel C35E (1.1181)
| EU EN | USA - | Germany DIN,WNr | Japan JIS | France AFNOR | England BS | Italy UNI | Spain UNE | China GB | Sweden SS | Finland SFS | Russia GOST | Inter ISO | |||||||||||||||
| C35E |
|
|
|
|
|
|
|
|
|
|
|
|
免責聲明
- 凡本網注明“來源：化工儀器網”的所有作品，均為浙江興旺寶明通網絡有限公司-化工儀器網合法擁有版權或有權使用的作品，未經本網授權不得轉載、摘編或利用其它方式使用上述作品。已經本網授權使用作品的，應在授權范圍內使用，并注明“來源：化工儀器網”。違反上述聲明者，本網將追究其相關法律責任。
- 本網轉載并注明自其他來源（非化工儀器網）的作品，目的在于傳遞更多信息，并不代表本網贊同其觀點和對其真實性負責，不承擔此類作品侵權行為的直接責任及連帶責任。其他媒體、網站或個人從本網轉載時，必須保留本網注明的作品第一來源，并自負版權等法律責任。
- 如涉及作品內容、版權等問題，請在作品發表之日起一周內與本網聯系，否則視為放棄相關權利。
采購中心